Nickel Alloy 200/201 Fasteners
Nickel Alloy 200/201 UNS N02200/N02201 Fasteners | Nickel Alloy 200/201 ASTM B564 Fasteners | Nickel Alloy 200/201 ASME B16.11 Fasteners
Nickel Alloy 200/201 ASTM B160 Fasteners | Nickel Alloy 200/201 DIN 2.4066 / 2.4068 Fasteners | Nickel Alloy 200/201 ASTM B472 Fasteners
Champak Steel Engg. furthermore, Co. is a Renowned and one of the most seasoned makers, stockiest and suppliers of Nickel 200/201 Fasteners, ASTM F 2281 Nickel Alloy 200/201 Fasteners. Nickel 200/201 Fasteners have unique quality completing and coercion for long life, high weight and zero imperfections.
The item separation depends on the chief completion of Nickel 200/201 Fasteners with least burr at the edge . The closures for flawless welding and manufacture of the Wire in super ventures in oil and gas industry for long existence of the item.
Specification
| Grades | Nickel 200/201 (UNS 2200/2201) |
|---|---|
| Standards | ASTM, BS, IS |
| Specifications | ASTM / ASME SB 160 / 164 / 425 / 166 / 446 / 574 / 472 |
| Size | M02 to M30 |
| Length | 3 mm To 200 mm |
| Types | Nuts, Bolts, Screws, Sockets, Studs, Screw, Hex Set Screw, Socket Screw, Cap Screw, Pan Head Screw, Machine Screw, Socket Head Cap Screw, Allen Cap screw, Wing Screw, Washers, Spring Washers, Studs, Anchors, Marine Anchors, Nut, Hexagon Nut, Hex Nut, Hex Coupling Nut, Hex Domed Cap Nuts, Square Nut, Stud Bolts, Hex Head Bolts, Socket Hexagon Head Screw Anchor Bolt, U- Bolts, J Bolts, Mushroom Head Square Neck Bolts, T-Head Bolts, Wing Screw, Eye Bolt, Foundation Bolts, Structural Bolts. |
Chemical Composition
| Material / Purity: | Alloy 200 | Alloy 201 |
|---|---|---|
| Ni | 99.00 | 99.00 |
| Fe | .40 | 0.40 |
| Mn | 0.35 | 0.35 |
| Si | 0.35 | 0.35 |
| C | 0.15 | 0.02 |
| S | 0.01 | 0.01 |
| Cu | 0.25 | 0.25 |
Mechanical Properties
| Nickel Alloy 201 | ||
|---|---|---|
| Properties | Metric | Imperial |
| Tensile strength (annealed) | 403 MPa | 58500 psi |
| Yield strength (annealed) | 103 MPa | 14900 psi |
| Elongation at break (annealed prior to test) | 50% | 50% |
| Nickel Alloy 200 | ||
| Properties | Metric | Imperial |
| Tensile strength (annealed) | 462 MPa | 67000 psi |
| Yield strength (annealed) | 148 MPa | 21500 psi |
| Elongation at break (annealed prior to test) | 45% | 45% |
Physical Properties
| Density | 8.902gm/cc |
|---|---|
| Melting Point | 1453 oC |
| Boiling Point | 2732 oC |
| Thermal Conductivity | 0.909 W/cm/K @ 298.2K |
| Electrical Resistivity | 6.84 microhm-cm @ 20 |
| Electronegativity | 1.8 Paulings |
| Specific Heat | 0.106 Cal/g/ K @ 25 |
| Heat of Vaporization | 91.0 K-Cal/gm atom at 2732 oC |
| Heat of Fusion | 4.20 Cal/gm mole |